Exportar este item: EndNote BibTex

Use este identificador para citar ou linkar para este item: http://tede.bc.uepb.edu.br/jspui/handle/tede/3307
Registro completo de metadados
Campo DCValorIdioma
dc.creatorAlves, Erica Silva dos Santos-
dc.creator.Latteshttp://lattes.cnpq.br/9765301552004731por
dc.contributor.advisor1Alves, Mary Cristina Ferreira-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/1408702023173864por
dc.contributor.advisor-co1Silva, Márcia Rejane Santos da-
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/7632449835328149por
dc.contributor.referee1Ribeiro, Danniely de Melo-
dc.contributor.referee1Latteshttp://lattes.cnpq.br/7022962252244940por
dc.contributor.referee2Nascimento, Marcelo Rodrigues do-
dc.contributor.referee2Latteshttp://lattes.cnpq.br/0089895788137645por
dc.date.accessioned2019-04-24T15:07:16Z-
dc.date.issued2017-12-19-
dc.identifier.citationALVES, E. S. dos S. Preparação de silicatos de cálcio: avaliação do potencial fotocatalítico. 2017. 64f. Dissertação (Programa de Pós-Graduação em Química - PPGQ) - Universidade Estadual da Paraíba, Campina Grande, 2017.por
dc.identifier.urihttp://tede.bc.uepb.edu.br/jspui/handle/tede/3307-
dc.description.resumoOs silicatos de cálcio são materiais cerâmicos que têm sido cada vez mais investigado por apresentarem excelentes propriedades como: biocompatibilidade, bioatividade, ótima resistência, permeabilidade. Sendo amplamente utilizados em aplicações tecnológicas, biomédicas entre outras finalidades. Apesar de serem encontrado em grande abundância na natureza, encontra-se associado a outros constituintes, sendo dessa forma, necessária sua produção sem contaminantes. Nesse contexto, o presente trabalho teve por objetivo a síntese de silicatos de cálcio pelo método dos precursores poliméricos, visando aplicação em fotocatálise heterogênea. A preparação dos silicatos (Ca2SiO4 e CaSiO3) foi realizada em três etapas de otimização, em que foi avaliado o tempo de tratamento térmico, concentração da solução de silício, bem como a variação da temperatura durante o processo de cristalização. A decomposição dos pós precursores foi avaliada por analise termogravimétrica (TG/DTG), e após a calcinação o material foi caracterizado por Difração de Raios-X, espectroscopia nas regiões do infravermelho e UV-visível. Podemos observar a partir dos padrões de DRX que o aumento da temperatura de cristalização e o tempo de calcinação, favorece a obtenção de heteroestruturas de silicatos de cálcio nas fases (Ca2SiO4 e CaSiO3) com excelente qualidade cristalina, sendo que a amostra tratada a 800°C por 8h tende a formar silicato de cálcio com a fase Ca2SiO4(larnita) em majoritariedade em relação a fase CaSiO3(wolastonita), enquanto que a amostra tratada a 900 °C por 8 horas apresentou comportamento inverso, ou seja, a fase CaSiO3 se apresenta em maior quantidade na composição da heteroestrutura. Os espectros de infravermelho das amostras de silicatos tratados em diferentes temperaturas e variados tempos de calcinação apresentaram espectros com perfis e modos vibracionais característicos dos sistemas Ca2SiO4 e CaSiO3, corroborando com os resultados de DRX. Adicionalmente, também foi observado um aumento gradativo do tamanho de cristalito em função da elevação da temperatura de tratamento térmico e do tempo de calcinação. Os testes fotocatalíticos foram realizados com o corante Remazol Amarelo Ouro, monitorando as regiões de degradação (238 e 292 nm) e descoloração (412 nm) por espectroscopia na região do UV- Visível. Os resultados apresentados foram bastante promissores com uma média de 78 % de descoloração e 44 e 21 % para degradação dos grupos aromáticos e ligações π-π* para a amostra Ca2SiO4/CaSiO3 com fase majoritária de Ca2SiO4 e 82 % de descoloração e 44 e 21 % para degradação dos grupos aromáticos e ligações π-π* para a amostra CaSiO3/Ca2SiO4 com fase majoritária de CaSiO3. Contudo, os resultados primários apresentados para estes materiais indicaram que possuem potenciais para aplicação em processo de fotocatálise heterogênea, sendo necessários estudos posteriores visando à otimização dos resultados obtidos.por
dc.description.abstractCalcium silicates are ceramic materials that have been increasingly investigated for having excellent properties such as: biocompatibility, bioactivity, optimum strength, permeability. Being widely used in technological applications, biomedical among other purposes. Despite being found in great abundance in nature, it is associated with other constituents, and therefore, its production without contaminants is necessary. In this context, the present work had the objective of the synthesis of calcium silicates by the method of the polymeric precursors, aiming application in heterogeneous photocatalysis. The preparation of the silicates (Ca2SiO4 and CaSiO3) was carried out in three optimization stages, in which the thermal treatment time, concentration of the silicon solution, as well as the temperature variation during the crystallization process were evaluated. The decomposition of precursor powders was evaluated by thermogravimetric analysis (TG / DTG), and after calcination the material was characterized by X-ray diffraction, infrared and UV-visible spectroscopy. We can observe from the XRD patterns that the increase of the crystallization temperature and the calcination time, favors the obtaining of calcium silicate heterostructures in the phases (Ca2 SiO4 and CaSiO3) with excellent crystalline quality, with the sample treated at 800 ° C for 8h tends to form calcium silicate with the Ca2SiO4 phase (larnite) in the majority in relation to the CaSiO3 phase (wolastonite), while the sample treated at 900 ° C for 8 hours showed an inverse behavior, that is, the CaSiO3 phase the composition of the heterostructure. The infrared spectra of the silicate samples treated at different temperatures and varying calcination times presented spectra with profiles and vibrational modes characteristic of the Ca2SiO4 and CaSiO3 systems, corroborating with the results of XRD. Additionally, a gradual increase in crystallite size was observed as a function of the elevation of the heat treatment temperature and the calcination time. The photocatalytic tests were performed with Remazol Amarelo Ouro dye, monitoring the regions of degradation (238 and 292 nm) and discoloration (412 nm) by spectroscopy in the UV-Visible region. The results presented were very promising with a mean of 78% discoloration and 44 and 21% for degradation of the aromatic groups and π-π * bonds for the sample Ca2SiO4 / CaSiO3 with Ca2SiO4 major phase and 82% discoloration and 44 and 21 % for degradation of the aromatic groups and π-π * bonds for the CaSiO3 / Ca2SiO4 sample with the CaSiO3 major phase. However, the primary results presented for these materials indicated that they have potentials for application in a heterogeneous photocatalysis process, and further studies are needed to optimize the obtained results.eng
dc.description.provenanceSubmitted by Jean Medeiros (jeanletras@uepb.edu.br) on 2019-04-16T13:48:50Z No. of bitstreams: 1 PDF - Érica Silva dos Santos Alves.pdf: 20729972 bytes, checksum: b72239aef0c8c951fb4a7ff2e825b483 (MD5)eng
dc.description.provenanceApproved for entry into archive by Secta BC (secta.csu.bc@uepb.edu.br) on 2019-04-24T15:07:16Z (GMT) No. of bitstreams: 1 PDF - Érica Silva dos Santos Alves.pdf: 20729972 bytes, checksum: b72239aef0c8c951fb4a7ff2e825b483 (MD5)eng
dc.description.provenanceMade available in DSpace on 2019-04-24T15:07:16Z (GMT). No. of bitstreams: 1 PDF - Érica Silva dos Santos Alves.pdf: 20729972 bytes, checksum: b72239aef0c8c951fb4a7ff2e825b483 (MD5) Previous issue date: 2017-12-19eng
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESpor
dc.formatapplication/pdf*
dc.thumbnail.urlhttp://tede.bc.uepb.edu.br/jspui/retrieve/8090/PDF%20-%20%c3%89rica%20Silva%20dos%20Santos%20Alves.pdf.jpg*
dc.languageporpor
dc.publisherUniversidade Estadual da Paraíbapor
dc.publisher.departmentPró-Reitoria de Pós-Graduação e Pesquisa - PRPGPpor
dc.publisher.countryBrasilpor
dc.publisher.initialsUEPBpor
dc.publisher.programPrograma de Pós-Graduação em Química - PPGQpor
dc.rightsAcesso Abertopor
dc.subjectSilicato de cálciopor
dc.subjectFotocatálise heterogêneapor
dc.subjectAzo corantespor
dc.subject.cnpqCIENCIAS EXATAS E DA TERRA::QUIMICApor
dc.titlePreparação de silicatos de cálcio: avaliação do potencial fotocatalíticopor
dc.typeDissertaçãopor
Aparece nas coleções:PPGQ - Dissertações

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
PDF - Érica Silva dos Santos Alves.pdfPDF - Érica Silva dos Santos Alves20.24 MBAdobe PDFThumbnail

Baixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.